Page 316 - Engineering Plastics Handbook
P. 316
(Continued)
7130 203 158 108 6 22.3 355 263 177 16.5 15.6 13.1 250 9.9 120 47 340 0.39
14
11
5030 205 160 113 7 15 12 10.8 338 251 184 11.7 10.7 9.9 260 7.9 140 79 504 0.43
4435 110 90 52 6 4 3 9.7 152 129 91 14.8 11.2 10.3 138 8.5 60 43 219 0.42
4275 131 116 56 7 15 17 7.8 212 157 111 7.3 5.6 5.1 120 4.0 77 84 250 0.39
4301 164 113 73 7 20 17 6.6 219 165 113 6.9 5.5 4.5 170 5.3 112 63 404 0.39
4203L 192 117 66 15 21 22 4.9 244 174 120 5.0 3.9 3.6 220 4.0 128 142 1062 0.45
Polyamide-imide Properties for Compounded Materials
Units MPa % GPa MPa GPa MPa GPa MPa J/m
test
ASTM method D1708 D1708 D1708 D790 D790 D695 D695 D732 D256
Typical properties ∗ , SI units Mechanical Izod impact strength (3.2 mm)
12.1 Tensile strength Tensile elongation Tensile modulus Flexural strength Flexural modulus Compressive strength Compressive modulus Shear strength Notched Unnotched Poisson’s ratio
TABLE 23°C 135°C 232°C 23°C 135°C 232°C 23°C 23°C 135°C 232°C 23°C 135°C 232°C 23°C
275