Page 224 - Corrosion Engineering Principles and Practice
P. 224
198 C h a p t e r 6 R e c o g n i z i n g t h e F o r m s o f C o r r o s i o n 199
K I SCC , K I H
Log ∆a K I C
∆t
Log K
(c)
K I SCC
∆a
Log
∆n K I th K I C
Log ∆K
(d)
FIGURE 6.47 (continued)
outage or shutdown. Unless it is found during an inspection that
the crack growth rate might end up in a failure before the next
outage (with some safety factor), remedial actions are usually not
taken [37].
K = s C a (6.11)
π
I c m