Page 250 - Engineering Plastics Handbook
P. 250
PPX640
PPX630
PPX615
1.08 1.30 1.19 — — 0.03 — — 506,000 (3.56) 13,900 (98) 11,500 (81) 8600 (60) 6 8 5 1,206,000 (8.48) 806,000 (5.67) 444,000 (3.12) 21,900 (154) 18,800 (132) 13,300 (94) 2.0 (108) 3.1 (165) 2.0 (108) 1.8 (96) 1.9 (101) 1.2 (64) 10.8 (576) 15.5 (827) 10.9 (582) 326 (16
Properties of Glass-Reinforced PPE/PP Grades
Property Water abs., 24 h at 73°F (23°C), % Tensile strength at yield, psi (MPa) Tensile elongation at break, % NI at −22°F (−30°C), ft⋅lb/in (J/m) HDT at 66 psi (0.45 MPa), °F (°C) HDT at 264 psi (1.82 MPa), °F (°C) CTE, flow −40 to 100°F, in/in-°F (m/m-°C) CTE, crossflow −40 to 100°F,
TABLE 9.13 Specific gravity Tensile modulus, psi (MPa) Flexural modulus, psi (GPa) Flexural strength, psi (MPa) NI at 23°C, ft⋅lb/in (J/m) UNI at −40°C, ft⋅lb/in (J/m) Vicat B, °F (°C) UL-94 HB, in (mm)
213