Page 271 - Biaxial Multiaxial Fatigue and Fracture

The Multiaxial Fatigue Strength of Specimens Containing Small Defects 255

Fig. 10. Comparison of predicted and experimental results for quenched and
tempered SCM435 steel specimens containing a hole of 90 pm in diameter.

150 8 I I I 1 I I I I I i 8 i
(d
a

Experimental fatigue limit:
- 0 500pmhole

0 50 100 150
Axial stress amplitude, a, MPa

Fig. 1 1. Comparison of predicted and experimental results for high
strength brass specimens containing a hole of 500 pm in diameter.