Page 741 - Corrosion Engineering Principles and Practice

692 C h a p t e r 1 5 H i g h - Te m p e r a t u r e C o r r o s i o n 693

Affected (mm) > 0.91 > 0.55 > 0.96 > 1.17 > 0.94 > 3.8 > 3.7 0.35 0.21 0.26 > 3.57 > I .73 > 0.59

1250 (°C)

Loss (mm) > 0.91 > 0.55 > 0.96 > 1.17 > 0.94 > 3.8 > 3.7 0.29 0.096 0.2 > 3.57 > I .7 > 0.59

Affected (mm) 0.41 0.2 0.49 > 0.68 > 0.94 0.29 > 1.2 0.23 0.22 0. I I > 2.7 > 0.6 > 0.55

1150 (°C)

Temperature Loss (mm) 0.18 0.18 0.43 > 0.68 > 0.94 0.24 > 1.2 0.19 0.041 0.075 > 2.7 > 0.6 >0.55

1095 (°C) Affected (mm) 0.36 0.033 0.26 0.097 0.39 0.067 0.29 0.19 0.17 0.058 > 1.7 > 0.69 0.37

Loss (mm) 0,089 0.01 0.23 0.058 0.35 0.025 0.226 0.14 0.02 0.025 > 1.7 > 0.69 0.33

Affected (mm) 0.145 0.015 0.018 0.025 0.025 0.028 0.033 0.046 0.11 0.028 0.36 0.21 0.058

980 (°C)

Loss (mm) 0.0178 0.005 0.01 0.01 0.01 0.01 0.01 0.023 0.01 0.01 0.315 0.14 0.033
(continued)

Alloy 263 188 25 150 6B 556 Multimet 800H RA330 S31000 S31600 S30400 S44600 TABLE 15.7