Page 221 - Engineering Plastics Handbook

SE1GNF2 HS2000X HS1000X SE1GNF3 1.24 1.23 1.31 1.23 — 0.070 0.060 0.060 11,000 (76) 9500 (65) 17,500 (121) 15,500 (107) 20.0 30.0 5.0 5.0 515,000 (3.55) 420,000 (2.89) 1,130,000 (7.79) 830,000 (5.72) — — — — — — 108 106 — 121 — — 2.4 (128) 2.5 (133) 2.2 (117) 2.0 (107)

Properties of Reinforced, Flame-Retardant Grades

SE1GNF1 1.16 0.070 10,800 (74) 5.0 580,000 (4.00) 17,400 (120) 104 — 1.8 (96) 1.3 (69) 298 (148) — 269 (132) 110 105 110 3.00 3.00 0.0017 0.0016 1.0E15 0.058 (1.47) — —

Property Water abs., 24 h at 73°F (23°C), % Tensile strength at yield, psi (MPa) Tensile elongation at break, % Flexural modulus, psi (GPa) Flexural strength, psi (MPa) NI at 23°C, ft⋅lb/in (J/m) NI at −40°C/F, ft⋅lb/in (J/m) HDT at 66 psi (0.45 MPa), °F (°C) HDT at 264 psi (1.82 MPa), °F (°C)

TABLE 9.4 Specific gravity Hardness, Rockwell L Hardness, Rockwell R Vicat B, °F (°C) RTI electrical, °C RTI with impact, °C UL-94 V, in (mm) UL-94 V-0, in (mm) UL-94-5 VA, in (mm)

192