Page 343 - Engineering Plastics Handbook

PPSF
Typical Physical and Mechanical Properties of Glass-Fiber-Reinforced (GR) Polysulfone, Polyethersulfone,
PES
PSF
10% GR 30% GR 30% GR 20% GR 10% GR 30% GR 20% GR 120 126 105 86 108 96.5 77.9 9.2 8.6 5.7 3.8 7.38 5.17 3.65 2.4 1.9 3.2 5.8 2.0 3.2 4.1 173 179 162 145 154 148 128 8.0 8.1 5.2 4.1 7.58 5.52 3.79 75 75 59 48 74 69 64 83 71 65 59 109 114

ASTM-test method D-638 D-638 D-638 D-790 D-790 D-256 D-1822 D-648 D-696 D-1505 D-955 to ft⋅lbf/in 2 , divide by 2.10.

and Polyphenylsulfone Property Tensile strength, Mpa* Tensile modulus, GPa † Tensile elongation, % Flexural strength, MPa Flexural modulus, GPa Tensile impact, kJ/m 2§ Heat deflection temp., °C Mold shrinkage, mm/mm * To convert MPa to psi, multiply by 145. † To convert GPa to psi, multi

13.5 Izod impact, J/m ‡ CLTE, mm/(mm⋅°C) Specific gravity
TABLE

301