PPSF 30% GR 120 9.2 2.4 173 8.0 75 83 210 — 1.53 0.003

Typical Physical and Mechanical Properties of Glass-Fiber-Reinforced (GR) Polysulfone, Polyethersulfone,
30% GR 126 8.6 1.9 179 8.1 75 71 216 3.1 1.58 0.003

PES 20% GR 105 5.7 3.2 162 5.2 59 65 214 3.1 1.51 0.004

10% GR 86 3.8 5.8 145 4.1 48 59 211 3.6 1.43 0.005

30% GR 108 7.38 2.0 154 7.58 74 109 181 2.0 1.49 0.002

PSF 20% GR 96.5 5.17 3.2 148 5.52 69 114 180 2.5 1.40 0.003

10% GR 77.9 3.65 4.1 128 3.79 64 101 179 3.6 1.33 0.004

ASTM-test method D-638 D-638 D-638 D-790 D-790 D-256 D-1822 D-648 D-696 D-1505 D-955 to ft⋅lbf/in 2 , divide by 2.10.

and Polyphenylsulfone Property Tensile strength, Mpa* Tensile modulus, GPa † Tensile elongation, % Flexural strength, MPa Flexural modulus, GPa Tensile impact, kJ/m 2§ Heat deflection temp., °C Mold shrinkage, mm/mm * To convert MPa to psi, multiply by 145. † To convert GPa to psi, multi

13.5 Izod impact, J/m ‡ CLTE, mm/(mm⋅°C) Specific gravity
TABLE

301